PLA Basic Filament

Diameter

●Versatile & Reliable Everyday PLA Designed for seamless compatibility with all mainstream 3D printers, delivering exceptional balance, ease of use, and cost-efficiency.
●Enhanced Toughness & Smooth Flow Specially modified for higher impact resistance and consistent flow, allowing for a wide printing temperature and speed range.
●Built for Fast & Large-Scale Printing Optimized flow rate and layer adhesion prevent warping or deformation—ideal for high-speed printing and large, complex models.
●Flawless Smooth Finish Produces clean, fine surface quality with visible line reduction on every print.
●30+ Vibrant Colors Extensive color palette available to bring any creative design or functional prototype to life.

Suggested Printing Parameters

Nozzle temperature	200~240 ℃
Bed temperature	35~55 ℃
Bed modification	PEI frosted board
Active cooling fan	ON, 50~100 %
Layer height	0.2 mm
Shell thickness	≥0.8 mm
Print speed	≤300 mm/s

Settings are based on a 0.4mm nozzle.

Technical Data Sheet (TDS)

Material Properties	Typical Value	Test Method
Melt temperature	~160℃	ISO 11357
Glass transition temperature	~60℃	ISO 11357
Melt flow rate (MFR)¹	5~10g/10min	ISO 1133
Heat deflection temperature (HDT)²	59℃	ISO 75
Vicat softening temperature (VST)³	73℃	ISO 306
Density	1.21–1.23g/cm³	ISO 1183
Odor	Odorless	/
Solubility	Insoluble in water	/

1. Test conditions: T= 190℃; m= 2.16kg.
2. Test conditions: 0.45MPa; 120℃/h.
3. Test conditions: 10N; 120℃/h.

Download TDS Shop Now ada apa

PLA Basic Filament

●Versatile & Reliable Everyday PLA Designed for seamless compatibility with all mainstream 3D printers, delivering exceptional balance, ease of use, and cost-efficiency.</br> ●Enhanced Toughness & Smooth Flow Specially modified for higher impact resistance and consistent flow, allowing for a wide printing temperature and speed range.</br> ●Built for Fast & Large-Scale Printing Optimized flow rate and layer adhesion prevent warping or deformation—ideal for high-speed printing and large, complex models.</br> ●Flawless Smooth Finish Produces clean, fine surface quality with visible line reduct...

membagikan：

Hubungi kami

Permintaan Online

Surat：zt@shjanton.com

ada apa：+86 13901946093



PLA RoHS REACH FDA
[Klik untuk mendownload]

Nozzle temperature	200~240 ℃
Bed temperature	35~55 ℃
Bed modification	PEI frosted board
Active cooling fan	ON, 50~100 %
Layer height	0.2 mm
Shell thickness	≥0.8 mm
Print speed	≤300 mm/s

Settings are based on a 0.4mm nozzle.

Material Properties	Typical Value	Test Method
Melt temperature	~160℃	ISO 11357
Glass transition temperature	~60℃	ISO 11357
Melt flow rate (MFR)¹	5~10g/10min	ISO 1133
Heat deflection temperature (HDT)²	59℃	ISO 75
Vicat softening temperature (VST)³	73℃	ISO 306
Density	1.21–1.23g/cm³	ISO 1183
Odor	Odorless	/
Solubility	Insoluble in water	/

1. Test conditions: T= 190℃; m= 2.16kg.
2. Test conditions: 0.45MPa; 120℃/h.
3. Test conditions: 10N; 120℃/h.